Scenario: A pressure vessel has four WPS/PQR. Three have PWHT, the 4th WPS/PQR does not have PWHT. All are valid WPS/PQR. After completion of welding, the whole pressure vessel goes into a furnace for heat treatment.
Question: Is this an NCR? Does the 4th WPS have to be requalified in...
This original post (thread725-19716) refers.
Backing gas is an NEV in ASME IX for GTAW, so changing the backing gas from Argon to Nitrogren does not trigger the requalification of the PQR (but of course, welders cannot change WPS by themselves, WPS can be edited by Welding Engineer without...
Is a pinhole considered a "rounded indication"?
As per ASME VIII Division 1 Mandatory Appendix 8:
"Rounded indications: any relevant indication (it means if its major dimension is greater than 1/16 (1.5 mm) ) shall be considered rejected if it is greater than 3/16 in (5 mm)"
As per ASME VIII...
Has anyone done a tube leak detection on shell and tube heat exchangers? The procedure is like this:
1. Pressurized shell side with pneumatic up to 4 barg, depending on your comfort level in handling pneumatic test.
2. Cover one tubesheet with masking tape, ensuring every tube hole is covered...
There is an ongoing discussion in my workplace regarding
SA 516 Gr. 70N vs SA 516 Gr. 70NACT vs SA 516 Gr70 Q&T
Which one is a better heat treatment for SA 516 Gr. 70? The requirement calls for HIC-resistant steel, too.
The group specifications mentioned "minimum normalized" condition for SA...
Dear all.
It is now 2020 and ASME PCC-2 2018 has been published with this paragraph:
"307-4.3.2 Cold bending refers to bending below Tcrit. The pipe may be bent cold if permitted by the applicable construction code or post-construction code. Cold bending may require heating below the...
For all intents and purpose, I was presenting a hypothetical case.
The point is this: which is more supreme. The NDT or the pressure testing?
Which act(s) actually certify, validate the integrity of a facility: the NDT or the pressure testing?
ASME B31.3 allows "closure weld" procedure for...
Allow me to be argumentative.
Hydrotesting is done to mimic the severest condition of operation. NDT in 99.99% of the time, does not in itself certify a facility.
There is no penalty by the Code if any NDT was not done or not done at all, unlike pressure testing which is compulsory and would...
For some reason, NDT was not done or carried out less than stated in ITP for a given equipment/facility.
However, equipment/facility was successfully hydrotested, and operated for almost 2 years without any incident.
Considering that NDT was not fully completed or not compliant to Code...
Hi there Ed. Thank you for your reply.
1. Yes it is under B423.
2. As per the mill certificates:
a. Cold finished
b. Delivery Condition: Annealed Pickled Passivated
3. Testing (all passed):
a. UT as per ASTM E213
b. Hydro as per ASTM B829
c. Etching test as per ASTM E381
d. PT for beveled...
Dear all.
We have an Incoloy 825 pipe, just received from the mill with internal surface cracks first detected by visual (plain eyes!) then confirmed with dye penetrant (PT).
Questions:
1. From ASTM B423 and then ASTM B829, it seems that these surface cracks would not be able to be detected by...
I don't quite understand the plot you shared but test results, by statistics, are "fit" into equations, either linear, quadratic, or more complex equations, to check for predictability.
This equation is then drawn through the test data results (or samples).
This is called statistical...
So a fabricator made a PQR based on these parameters:
T = 50 mm
GTAW t (root) = 8 mm
SMAW t (middle passes) = 21 mm
SAW t (subsequent passes plus cap) = 21 mm
The PQR above is used to support a WPS with SMAW only and T and t ranges of 8 mm to 200 mm. (The WPS stated backing is required but this...