Hi,
I think it maybe due to the resin itself. The wet condition doese weaked the resin/fiber interface that's why you get lower stress and IPS number. But it may not soft your resin matrix so you didn't have a drop on modulus. Or the Wet Tg of the resin is much higher than your test temperature...