now i see, thanks gtaw, make sense to me now.

Don56,metengr,edstainless,dhengr. Guys thank you for the idea now probably i can now locate the root cause of this failure. The root weld is out side of the form head, so it is in the form of tension while the bevel is in form of compression. Does the root of the weld has effect facing...

Thank you metengr. And edstainless. My apology not to mention the material thickness it is a 12 mm stainless plate 304L. Alongitunal crack occured it was a single bevel edge preparation 3mm root face 3 mm root gap 60 degree angle. We ust ndt. Dye penetrant and ultrasonic test to check if there...

Hi guys. I have a project stainless Hooper, now for the dish head cap, i used welding electrode E308-17 and on the other weld side SW-308L CORED for flux core welding with complete joint penetration material 304L. after the weld process we undergo dye penetrant testing and it goes well. now...

Thank you metengr. great help.

I was using the water based. But not much effective. I will try the idea of metalfixer. Anyway guys thank you so much for the idea.

Hi Guys. What is the best Brand for anti welding spotter in welding stainless steel. Thank you in advance, have a nice day.

Thank you Metengr. But i just want to clarify. He is not an Employee of the organization but a Certified welding Inspector by CSWIP 3.1 3.2 he just got a course and take exam, then passed the 3.1 and 3.2 CSWIP course can he Qualify directly the documentation of PQR/WPS following the governing...

Hi. Can a CWI or CSWIP PERSONNEL qualify a WPS? please send your advice Thank you in advance.

HI. Can the CSWIP OR CWI Welding Inspector Qualify the PQR/wps..or need 3rd party to qualify the PQR for submerged arc welding (SAW)