Hi, btrueblood We are planning to add silicone grease on rubber and heating the assembly in chamber to see if it can eliminate the adhesion problem.

Hi, TugboatEng Yes, we purchase this solenoid and assemble it to AL base. PTFE coating on trading part may not be good since it need be sent out and processed agian.

1st pic showed rubber stick to AL. You can see armature did not fall off under gravity. Pic 3 showed appearance of sealing rubber after contacted with AL under pressure of solenoid spring. This solenoid is normal closed, FKM seal is to seal this hole. There is only air in base. Power on the...

Hi, I got problem that FKM seal will stick to anodized aluminum after 9 days` chamber test(-30degree 5%humidity for 72h,40degree 90% for 72h, 60degree 5% humidity for 72h). This lead to failure of movement for armature. Any guys know the reason of this stick issue and how I can avoid this...

Hi I have got problem that there was breakage on torsion spring. It occurred on end, but in previous REL test it occurred on squeezed part. See attachment. I am a little confused about these two failures. I want to improve design to distribute stress on end of spring. And considering to add two...

Hi, everyone We have a product that can peform determinations of nitrogen/protein according to the Kjeldahl method However we found recovery rate was a little low recently. See below steps: 1. H2SO4 + K2SO4 + catalyst → NH4+(AcidicSolution) -------Digestion in 420℃ 2. NH4 + NaOH + steam...

Hi, all We have a safety door that can provent steam hurting the customer, but seems the material was not strong enough. The material is PMMA whhle there is crack after used for less than 1 year. See links. Sprayed solvent on safety door: 40% NaOH + 100℃ steam Problem: There is crack on...

Thx for your comments![thumbsup2] I will check again in supplier side.

In the first time I also guess it was caused by pressure in cabient during foaming, but last week I went to supplier to check foaming and found one cabient had shrink on side surface.It is a little hard to explain this defect. Yesterday I took one cabient and put it in the chamber to heat in 45...

Hi, all. We have a cabinet that is finished by foaming in mould. We got problem that top surface drumed and sheet metal peeled off from foaming. It looks like there is air between them. below is product information: Cabinet material: Sheet metal- EN1.4301 (t=1mm) (length=725mm height=600mm...