When is required that all plates shall be supplied using the thermo-mechanical control process (TMCP), automatically the supply status of the material will be the type thermomechanically?
If it instead the plates to be transformed into pipes, instead talking about Thermomechanically rolled? Is...
Thank you Jones.
So is correct to consider that after tensile test the difference between weld material and the base material must be as minimum of 80MPa.
Dear All,
The 80MPa of difference that this paragraph asks between base material and weld material, are to be considered after mechanical test or data Nominal tensile?
Thank you in advance,
Emilio A.
Thank you...
So for example the following composition in weld areas may be acceptable:
Cr = 19.490
Ni = 43.570
Mo = 6.828
Nb = 2.411
Fe = 23.500
There is a reference in the Code governing these limits?
Thanks,
Emilio A.
Hello weldstan,
Thanks for your cooperation.
If I welding the B729 N08020 with the filler metal ENiCrMo-3, which chemical composition can I expect when I do the PMI (Positive Material Identification)?
The Code Project is ASME B31.3.
Grazie,
Emilio A.
Hi,
I can weld the B729 N08020 with the filler metal ENiCrMo-3?
In the analysis of the chemical composition which composition must be taken into consideration, that of the filler metal or the base material?
Thank you all.
Emilio A.