Yes, I do have scrap parts same condition TDH4 and same base material [glasses] I checked the graph i attached on previous comment and I will go for 700F for 3 hours and 30 min and see what I get. [glasses]

600+/-25F for 2 hours were use for aging them. So do you think that at 600F for 30 min with work? or 700F for 15 min? According the picture below to make it more ductile? Thank you, :) https://files.engineering.com/getfile.aspx?folder=b41e9cc0-891e-48ac-8db7-7a9f848ebbb1&file=1.png

Thank you EdStainless! Alloy is 25 and it is cold worked. :( my main goal is 30-35HRC no matter other properties

Hello, I have Full Tempered (TDH4) Beryllium Copper that is on the range of 35-42HRC and I want to soften it to 30-35HRC, I know Age Hardening Temperature is 2-3 hours on 600's°F but this will be my first time softening. I am not sure if more than 3 hours Work Zone time will softer them. If...