Just I am wondering if we go for Q&T process with recomended alloy(1040,4140,...), doesn'it affect our machining process?( which needs to be done after Q&T application).
Yes, Exactly it is a plastic deformation and it is hapening after dynamic application.So if it is the case if there is any substitude material with higher TS and suitable for machinning?
Hi There,
I recently joint the group and I came up with following issue which very much related to material selection and applying the right heat treatment. we are using A.I.S.I 1144 steel for our starter armature shaft (.8225/.8240')and carburising the full length of spline to R/C 48/55 (depth...