Hey,
After getting some help from our great members with my problem of finding a good core for my magnet, i have decided to anneal the steel i am using (1018) in order to restore/improve the properties of it after i machine it.
Any one have any experience with this process?
Can maybe direct me...
thanks guys, MagMike, i'm not sure I want to start dealing with heat treatment beofre I can use it.
but MagneticIronGuy, your ideas might work.
thanks a lot
thanks for the info.
It is for a DC application.
Do you (or anyone else) have a good idea for something else that I can use instead of 1018 with a higher mu?
Thanks
Hi everyone,
I am building a magnet that will go into vacuum. It must be small (chamber limitations) and reach 0.1T
As of now I am using steel 1018 but read in a journal that 1010 was used with better results.
I can't seem to find anywhere to compare these too steels (mu and other parameters)...