I need your help.
Plate Material : 1) SA 516 Gr 70 (Normalized)
Thickness : a) 19 mm and b) 12.5 mm
Minimum design temparature : Minus 50 Deg. F
Is impact testing is require for 1a and 1b.
Your help will be appreciated.
Thanks for both the inputs. However the internals shall be placed through the dished end opening and after the internals are welded, dished end also welded. The whole vessel shall be PWHT. The internals are welded inside of the shell and not bolted. Based on the size of the internals, it not...
Currently I am designing on ASME section-VIII Div-1 (Code)drum with 'U' stamp. Drum is SA 516 Gr 70N and the shell and head thickness approximately 80 mm. Stainless steel SS 316L internals are placed inside drum. The fabricated drum shall be PWHT as per the Code. The SS 316L internals are welded...
I have seen in the internet, a pressure vessel drawing showing the various ASME code sections. FOr example if I move the cursor to nozzle it will show the correct UG section of the ASME code, if I move the cursor to tubesheet it will show the ASME code section to be followed. But I don't know...
Thanks for the reply.
However, what is exact difference between the two i.e Div-1 and div-1. Is there a ready reconer availabe or anyone can help me this ?
Currently I am involved in the design of pressure vessel. Thickness of vessel is approximately 5" (SA 516 Gr 70 N), designed for ASME section VIII div-1. If I have to go to fabricator for ASME section VIII - div-2 design, what are the things I have to consider in the design, fabrication...
Currently I am involved in the design of pressure vessel. Thickness of vessel is approximately 5" (SA 516 Gr 70 N), designed for ASME section VIII div-1. If I have to go to fabricator for ASME section VIII - div-2 design, what are the things I have to consider in the design, fabrication...