Dear Syedabbas, I think that CPT in wrought 22Cr DSS should be slighty higher than 22°C, so if the samples have failed G48 or A923 Met. C tests at that temperature is clear that the microstructure have been affected. I would try to cut the tested specimen through the cross section (BM-HAZ-WM)...