I am highly skeptical that this is really happening but quality says they have data to support part shrinkage. Has anyone ever ran into something like this before? We have 1043 hot rolled steel, .587" diameter and 5.5" long. We induction heat treat 1.375" on both ends to 48-52 Rc...
What is spheridized and non-spheridized steel? We have bar stock that is 1043 steel per MS-514 which calls out for a killed fine grain steel and it was mentioned that we also want to specify the material to be "non-spheridized". What is it?
Thank you,