I was in charge some days ago, by the company to manage the retrofit and relocation of a BFK 150. All the papers were lost, so I don't have any information. If anywone can provide any information, sketches, drawings, technical specifications would really help. Thanks a million!

Thanks. Sorry for your time. I'm quite desperate now.

it doesn't work. I just have microsoft word 2007. Can you convert it for me. It is attached on my first post. Thank you!

Preheating and heat treatment is mandatory. But at that level, i'm very affraid of cracks or lack of fusions. I have to check every weld ultrasonically.

ok. Thanks.

I have a casting for reparation. The C is 0.43%. will be a nightmare to weld it?

Can anyone tell me the maximum C content for material BS 3100 BT1. Thanks!

I have a file with .pwi extension. It is generated by a software for 3D measuring. I can not open it. I don't know if my part is wrong or right. My customer needs a proof that my machine is OK so we can validate the process. I can not open the file :((((( It's the second part i deliver. The...

Sorted out. I checked with the customer. It is 13CrMoV4. Thanks. I feel stupid now. It was my first post. But it helped.

Hi All, I have to make some rolled rings (70 mm thick) 2.5 m diameter. The only thing that i know about the material is 13CrV4. I can't find it. Can anyone give me any info. I need the mechanical proprieties to see what would be the force needed and if there are any risks for cracking. I need...