Would need too do a lot of reading up on corrosion inhibitors as I've never used them before, do they not just slow corrosion down slightly anyway?
I think salt water on its own would corrodes silver.
about 10 litre inner volume, streached cubiod shaped.
quick reply!
plastics are out as they are not compatable with the rest of the system, otherwise would be ideal!
temp <100 degrees, atmospheric pressure and no stress, although the system will be agitated.
yes just NaCl.
tantalum/silicon carbide coating overkill? bit costly...
thanks
Hi,
I'm trying to develop a material that will be stable in a aquous mixture of 10% graphite and 40% wt. chloride salt. It should have a low dissolved oxygen content due to being sealed. As you can imagine, quite corrosive! - plastics not an option.
Where's the best place to start?
Nickle...