Thanks Guys.
So if I mag partical inspect these and there are no cracks, after the manufacturing processes are complete (Grinding), I should be able to put them into their end-use applications and they should perform as air quenched A6 would have performed. Is this correct?
I am looking for information on the affects of oil quenching AISI A6 material during heat treatment rather than using air to quench. I would like to know just how negatively this will affect the mechanical properties of this steel?
By using an oil quench, has this completely destroyed the...