Thank you so much for your replies, I'm still waiting for the actual report done by our NDT contractor. We were just told initially that it failed and we need to gouge out our joints. Yes its Ultrasonic Testing I apologize for confusion.

hi guys, I would like to ask what normally causes a UT test failure?

hi steve, Thank you for your reply I would just like to clarify, does it means that this values from the impact test temperatures will define which temperature I can build or use a certain structure?

Hi guys, I would like to ask if an H beam structure EN10025 S355JR would be applicable for -20deg C or lower temperature area? Thank you very much.

Thank you very much for your reply. I find your info justifiable.

Good day guys! i would like to seek your expertise in API 8C Spec elongation requirements vs mill certs elongation. I find most suppler mill certs gave 31%-35% range which doesnt meet criteria of 23% from API 8C, shall i consider this for fabrication? thank you very much.