Hold the two aluminum pieces together in an insert molded part. Aluminum for rigidity of some of the external tabs. Chris Loughnane Mechanical Engineer Farm

@mcgyvr I see what you're saying, you are right. I feel silly. I may be able to split my parts into two so that there is only one trace per mass of aluminum. Given that, the result I am trying to achieve is a conductive, corrosion resistant individual trace on a metal. Since metal is...

@1gibson The two traces would not be electrically connected. @mcgyvr I understand that the bulk body is electrically connected, but it is my understanding that current is a surface phenomenon so that if (for example) I masked off two circles during a type III anodizing process that holding a...

I've got a design in my head that I think works, but I'm wondering if there are any gotchas Processing looks like this: -Part is aluminum 6061 -Mask is applied (contains two separate traces) -Type III anodization is performed (leaving raw aluminum where masked) -Type II anodization is...