My company is looking at developing a dome lamp that will be used inside refrigerated units. Is there an SAE or ISO standard that I can reference to see what the industry testing requirements are?
Does anyone know the industry standard that refers to the hose used on TPM systems used on trailes? I've searched in the SAE website, however I have not been successful to locate one.
My boss has requested that we replace a steel bolt with a nylon bolt. The nylon bolt will be used in an outdoor application where it will be subjected to many pulling forces, and different environments all across North America. Is there an accelerated weathering test standard that I can...
Hi all, my company purchases a zinc die casted part that recently has had a flash issue. The supplier states that the part meets drawing specs and is refusing to rework the parts unless we pay a service fee per part. As I reviewed the drawing I noticed that in one of our notes it states "FLASH...
We are in the process of looking to eliminate "Hexavalent" from our yellow chrome finish parts. I need more information on Zinc Trivalent Dichromate Plating. How many hours of salt spray can the Zinc Trivalent Dichromate Plating withstand? 72hrs, 96Hrs or 120hrs?
What would be an industry...
Metengr & TVP, thank you for your feedback. We are not planning on doing and significant deformation nor use this for magnetic purposes. I don't see why we can't accept what the supplier is suggesting. Thank you once again for your help.
I have a supplier that is asking to add JIS C3602 as an alternative material to C36000 brass, which we have always spec'd on our drawings. They provided a detail breakdown of the properties and I noticed that the JIS C3602 iron content (fe) was higher by .15%.
Will a higher content make the...