Good Morning All
I need help with clarification on Figure 100.1.2-3 in ASME B31.1-2018 pg 5.
I am bolting up a level radar transmitter past the double-block valves that come out of the steam drum on the boiler. I am being told due to the nipple we welded at the bottom of the housing had to be...
Good morning,
I was hoping I may be able to get some very helpful information on this API 4G, I've read the spec from front to back. I was just wondering if there is any other things I would need to know. Any advise y'all can give me will be greatly appreciated.
Thanks in advance
qcpeewee
Good day.
I was wondering if y'all can help me by giving me some information on a FCAW filler metal for API X65. I was wondering if E71T-1 would be sufficient or would it be better to run E71T-1 for root and hot pass and the run E80T-1. Any help would be greatly appreciated.
Thanks in...
Hello everyone.
I have some questions on some QPQ items on an assembly I have built. Question is, Will any of the items be effected if I weld on the assembly it's self? As in we would have to pre-heat to 125°F. Now where the preheat will be applied isn't QPQ although parts that are QPQ are in...
Hey guys I'm looking for some guidance on running a welding procedure on api 2h gr50 to 316ss and it requires charpy it is to AWS d1.1. Or should I be looking in AWS d1.6? Help please.
Thanks in advance
Qcpeewee
Hello again.
I have a question but not sure if it pertains to AWS D1.1. How many times can you carbon arc gouge welds before actually have to replace the steel where repairs are being made. Now is there a code or spec. I can look at to help with guiding me in the right direction.
Thanks in...
Question for you guys.
On A572 gr. 50 and A514 steel.
Is it allowed to heat the steel and put wet rags on it to stop it from moving anymore. Or is it best to let it air cool and hope it doesn't move go past where you want it.
If you run a wps on a514 1" thick plate in a 3G position without cvn in accordance with AWS D1.1 . Does that mean the wps is qualified in vertical position only 3G and 3F. But the welder is qualified in flat, vertical and horizontal. And the thickness is from 1/8"-unlimited. Can anyone please...
Hello again
Quick question. in AWS d1.1 2010 I tried looking to see where it states that after PWHT if NDE is required or not.
some people say only if its stated by the customer. I was always used to pre and post NDE. If ya'll don't mind clearing this up for me.
Thanks in advance.
Hey guys I need some clarification on a weld symbol. If I have a single v-groove symbol with no contour line or size of reinforcement and doesn't give anymore information does that automatically tell me to just fill in the groove flush or should I fill and add the 1/8" max reinforcement per AWS...
Hello
I was wondering if anyone knew a formula or a better way to find out how many ipm on my wire speed to calculate my amps. Before actually running it on my test.