Is 316 SS grade suitable for piping and equipment which will be exposed to ammonium sulfate slurry? At what flow velocity will erosion become a concern? I know there are several factors to consider including concentration of crystals, geometry of crystals, geometry of piping, temperature of the...
I would appreciate some input from the corrosion engineers here. If i have hydrogen gas flowing into a vessel, can it dissociate into atomic hydrogen and lead to hydrogen embrittlement, or does the hydrogen already have to be in atomic form (i.e. be the result of a corrosion reaction)? All input...