Dear Experts,
Please help. why does the ASME SEC 9, in there material list with correspond to P-no (parent number) & group Number, that some materials are not listed. what is the reason why does those material are not included in ASME SEC 9 QW-422
In my case.. Im using ASTM A707 it is not...
Dear Experts,
Please help. why does the ASME SEC 9, in there material list with correspond to P-no (parent number) & group Number, that some materials are not listed. what is the reason why does those material are not included in ASME SEC 9 QW-422
In my case.. Im using ASTM A707 it is not...
Hello all
Need your career advise.
I'm a licensed Mechanical Engineer from Philippines an Asia third world country, For 8 years I have been work in Middle east for Different Oil & Gas construction project as a Quality Inspector for Mechanical, Piping & Welding. I had also other certification...
Mates
Our project uses 2 code in WPS which qualified to ASME SEC9(for Piping) & AWS D1.1(for Structural)
My question is if welder is only qualified in AWS D1.1 for 3G position, can he do welding for ASME SEC9 Same 3G position & parameters (Dia, procecess,Thickness,F6 & Pno.) or vice versa...
Mates.
Good day1
Please inquire how to calculate pre-heat temperature using only CE value regardless of thickness.
Any references in ASME can be use as guide or other particular book.
Thankyou
Mates,
Please help. My PQR done was failed in hardness and impact test.
Details was
API-X60 Pipe(P1,Gr2)-16 inch Dia, 23mm Thick
Flange - A707 CL3 L5,(Not included in ASME sec 9 material grouping),16 inch Dia, 23mm Thick
GTAW-ER70S-2 -ROOT PASS & HOT PASS
SMAW-E7018-FILLING & CAP
CODE B31.8
NO...
Guys
Need your help, I will be conducting WQT by next week with our WPS that is qualified for API X60 PIPE and A707 CL3 L5 FLANGE. API X60 IS P1 GR2 and A707 CL3 L5 FLANGE does not have Pno assignment as per ASME SEC 1X
question? can we have substitution in WQT. instead of A707 CL3 L5 FLANGE...
Dear,
Please ask your technical expertise regarding the Difference between asme sec 9 and B31.3 for thickness qualified range iF impact test is required and not
DATA:
Test coupon is 12.7 mm if
1)Impact TEST NEEDED WHAT THICKNESS RANGE QUALIFIED? for SEC 9 & B31.3
2)IF NON Impact TEST NEEDED...
Guys,
Need your help regarding the impact test recently done. Please be informed for the ff
1) Design Temp is -28
2) Test coupon is 12.7 mm, API 5L X60,
3) Gtaw & Smaw Process
4) SMAW Size for impact test is 10x10x55
5) Gtaw size for impact test is 2.5x10x55
6) Both are done using -28 test...
Guys,
Need your help regarding the impact test recently done. Please be informed for the ff
1) Design Temp is -28
2) Test coupon is 12.7 mm, API 5L X60,
3) Gtaw & Smaw Process
4) SMAW Size for impact test is 10x10x55
5) Gtaw size for impact test is 2.5x10x55
6) Both are done using -28 test...
Dear Sir/madame
Please ask your assistance regarding your point of view for welding of 16" Dia, 22 mm Thick A707 CL3 L5 FLANGE to API 5L X60 Pipe, B31.8 code using ER70S-2 & E7018-1 ( GTAW & SMAW)
Facts:
1) As per B31.8 less than 32 mm Thickness does not require PWHT
2) As Per ASTM API 5L X60...
Dear Sir/madame
Please ask your assistance regarding your point of view for welding of 16" Dia, 22 mm Thick A707 CL3 L5 FLANGE to API 5L X60 Pipe, B31.8 code using ER70S-2 & E7018-1 ( GTAW & SMAW)
Facts:
1) As per B31.8 less than 32 mm Thickness doesnot require PWHT
2) As Per ASTM API 5L X60...
Dear Sir/madame
Please ask your assistance regarding your point of view for welding of 16" Dia, 22 mm Thick A707 CL3 L5 FLANGE to API 5L X60 Pipe, B31.8 code using ER70S-2 & E7018-1 ( GTAW & SMAW)
Facts:
1) As per B31.8 less than 32 mm Thickness doesnot require PWHT
2) As Per ASTM API 5L X60...