I have a consultation regarding the bending test of titanium alloy welding
ISO 15614-5
Quote
The diameter of the former or the inner roller shall be 6 t except for material group 51 when 4 t shall be used. The bending angle shall be 180° for parent metal with elongation A ≥ 20%. For parent...
For the tensile test of steel, tensile specimen with the full product thickness should be performed.
Particularly on very thick products where the capacity of the available testing machine is insufficient to allow the use of test specimen of full thickness, this may be reduced by machining one...
ISO 15614
8.4.4 Filler material, manufacturer/trade name, designation
Quote
For level 2: Filler materials cover other filler materials as long as, according to the designation in the appropriate international standard for the filler material, they have quivalent mechanical properties, same type...
Do test piece for Welding Process Qualification testing need to be carried out by qualified welders? Is it allowed that test piece weled by unqualified welders? Thank you.
It was noticed a post on the forum in 2006 about the 200 series austenitic steel, unfortunately I am unable to reply at this time. Eighteen years have passed, and it is unclear to what extent the 200 series austenitic stainless steel has been applied. Recently, there have been applications for...
Range of filler material for welding procedures qualification in ISO 15614-1
ISO 15614-1, 8.4.4 gives the following requirements,
Quote
For level 2: Filler materials cover other filler materials as long as, according to the designation in the appropriate international standard for the filler...
the following requirements for welding procedure qualification tests were given in 8.3.c) of EN 13445-4.
Quote
Impact test: The testing and the acceptance criteria shall conform to EN ISO 15614-1:2017; in addition, the impact test requirements in accordance with EN 13445-2:2021, Annex B shall...
Post-weld heat treatment may result in a reduced strength of the welded joint（Including base metal, heat affected zone, and welding consumables ）.
Even for some high-strength steels such as ASTM A517, the impact energy of welding consumables will decrease after post weld heat treatment.
What is...
Quote
ISO 4990-2023
6.2.2.1 Test blocks
The test blocks may be cast separately, attached to the castings or cast integrally on the castings.
Unquote
How to define and interpret the three test block types?
We have tried to give an explanation of the three types of test blocks, but we don't...
Whether the welded joint has a ductile - brittle transition temperature or not. The transformation temperature is usually considered to be for the steel itself, however there is literature on testing the transformation temperature of welded joints, so do welded joints also have a transformation...
What standards should be followed for Welding procedure qualification of stainless steel used for corrosion resistant services.
Mechanical tests are required in ISO 15614-1,ASME. No corrosion tests are required in ISO 15614-1,ASME.
For Stainless Steel for corrosion resistance service...
Hello，
ISO 15614 8.3.4
a) butt welds qualify full and partial penetration butt welds and fillet welds, while fillet weld tests are required where T-joints are performed by fillet welds or partial penetration butt welds in the pre-dominant form of welded connections in relation to the design and...
In EN 13195,it is specified that aluminum alloys supplied in the H116 or H321 temper in the form of sheet, strip and plate shall be subjected to exfoliation corrosion test and intergranular corrosion test. For H112 aluminum alloys supplied in the Otemper H111temper H112 temper, no corrosion test...
High-pressure water jet technology and wet blast technology have received extensive attention and application due to its high efficiency and environmental protection characteristics.
SSPC TU 1 defines surface-tolerant coatings which are suitable for wet blast or high-pressure water jet...
Methanol is corrosive to certain materials, however, opinions vary on which materials are compatible with methanol.
For example,
(1) can aluminum alloys, bronze, copper alloy, cast iron, nickel steel, galvanized steel, lead alloys, etc. be applied to methanol fuel systems(methanol tank...
Is there any guideline for repair for stainless steel pitting, such as (1) if excavating pitting, what should be the ratio of diameter to depth of the excavation to ensure a smooth transition. (2) For deeper pitting, is it possible to use a non-metallic filler such as epoxy putty without...
Clad steels with a clad layer from 316L, 317L or 317LN have been used in the shell of the ship.However, the PREN value of 316L, 317L or 317LN is not higher than 40.In this case, is it appropriate to choose 316L 317L or 317LN with PREN less than 40 as the side shell of the ship with long-term...
In ISO4990-2023,the test blocks may be cast separately, attached to the castings or cast integrally on the castings.
In ASTM A781, test coupons may be cast integrally with the castings, or as separate blocks.
How to understand the test blocks casting integrally on the castings? Does Cast...