I would like to know is there a possibilty to use R.O. 2nd pass as make up for an open recirculating cooling tower. if yes, what would be the best treatment chemistry and if not why not?
Thanks for youe help.
I was told that nitrite cant be used for open recirculating cooling towers.
Is it becuase oxygen will convert it into nitrate whihc dont have good inhibitor properties? I will appreciate if someone can explain in details.
Hi all.
Need help to decide b/w calcium hypochlorite and bromine tablets.
Need your experience. Please help me in comparison technically. I know there is no comparison comercially.
Thanks