Thank you very much for the prompt response. I really appreciate it. Instead doing solvent welding with formic acid, what do you think about melting the contact area with heat while feeding scrap of the same material into the joint?
Hello everyone. I have small personal project that I would like some help on. I need to join two piece of glass filled nylon with not a lot of surface area to work with. The joint needs to withstand 200+ degrees Fahrenheit as well as some impulse energy. My primary question is should I use...