If I understand the numbers/equation correctly there is no error in the standard, 1X is correct. Using the mean intercept method you only need to use the first equation to calculate your grain size. I believe your length IS in mm at 1X, that is to say although you may view it at 30X you use the...
Sorry, I should have been more specific. We have run into some issues with a couple of our Martensitic grades, I am checking into whether the issue is with the annealing and heat treating. I found some basic information on the grades in question including suggested heat treatments, however was...
In particular Martensitic SS and Precipitation Hardening SS, and for Duplex SS and for other detrimental phases in Austenitic SS as well.
I am a recent grad, so I guess I am not really sure what I am looking for. I am working on heat treatments, mostly annealing not as much aging, and trying to...
Does anyone know of a good resource for TTT/CCT diagrams for Stainless Steels?
My boss asked if there were any resources that would be of help to me. I checked out the ASM site and found the "Atlas of Time-Temperature Diagrams for Irons and Steels," but after finding the table of contents...