I will look in to it if that is the case or not.

Thank you ironic metallurgist. A WPS can be made with impact test mentioning ER80S-Ni1 when the PQR is qualified with 80S-Ni2. This is my question that what could be the possible options without qualifying a new PQR.

What could be the possible solution without qualification of new PQR?

Dear Experts, I have PQR for LTCS with filler wire ER-80S-Ni2 with impact test at -46C. I need to prepare a WPS for sour gas piping project with impact test at -46C which require nickel content should not be more than 1% in welding consumable. So considering the requirement of QW-404.12 if I...

Dear Gurus, The newly added Appendix C4 in ASME Sec.I 2017 addresses the preheat and pwht requirements for P No.15E. It refers to table C-4-1 for soak band, heating band and GCB. I am confused regarding heating band and soak band. If I fulfill the minimum requirement of heat band requirements...

ASME Sec II Part-A SA 182 Clause 18.2 says "following test reports required WHERE applicable" How one should assess whether product analysis is applicable or not? My product is conc.reducer and tee SA 182F91

Dear XL83NL, Yes they are as per SA-182F91 for boiler piping

Dear Experts, I had to verify MTRs of 1" Sch-160 tee and concentric reducer 3" x 1" Sch-160 material SA-182 F91. NDT mentioned on MTR is Magnetic Testing only. I have following queries: 1. As per SA-182 Clause 13 , NDT is required for DIN 100 and above. Is it true? 2. Are there any hydrotest...

Dear Members, I am working on a cross country water pipeline passing through some deserts and villages with population less than 100 people. Design code is ASME B31.8 and for welding and testing referring to API 1104. As per design 10% RT is required but the repair rate is almost 24%. Like we...

Respected researchers and experts, I am working for coal fired power plant where all the subjected materials are being used. Following are my questions please guide me: 1. T-22 and P-22 are similar in regard to welding metallurgy and pwht requirement? 2. T-91 and P-22 are similar in regard to...

Dear All, I am facing a problem for boiler tube RT. The dia of the tube is 38mm and space between adjacent tubes is that you can insert two fingers. Our contractor is using X-ray tube and it is impossible to do DWSI as source placement at 90 degree is really not possible. The contractor is not...

Dear All, I had started working on a coal fired water tube boiler for power plant. There is a confusion in contract that main boiler is designed on ASME and rest of the parts on GB standard. Following are my queries: 1. What are the boundaries of boiler? Do economizer, super heaters and...

We are using GE Technologies MIC 10. The material we are testing is A-333 Gr.6 and A 350 LF2. And some lines are of A-106 Gr.b and A-105. That is the reason we are not understanding the issue, the so much difference between two type of readings.

Dear and Respected, We are performing hardness testing of field sour line piping joints. Is it possible to take hardness of weld cap? Our WPS got qualified with hardness of 225(Vicker). Our project requirement is 248max. Now the scenario is for weld joint hardness value come around 262 and in...

Can you please elaborate the B31.3 2012 Clause 331.1.3 b).? 1. On what thickness we need to PWHT the pipe supports? 2. If the pipe joints need to be PWHT, the supports welded to them shall also be PWHT? 3. What does "thickness through the weld in any plane" means?

We are planning for PQR having following specs: Material : SA-333 Gr 6 to Sa 350 LF2 Cladding : Inside and weld joint Alloy 825 Groove to qualify: 14.27 to 24 mm Process : GTAW : up to 10 mm SMAW : from 11 to 24 mm My questions are: 1. As per ASME Sec.IX QW 453 tensile testing...

We need to weld A-106Gr.B and A-333 Gr f with A-320 TP 316L pipe. The filler wire to be used will be of 309L? If yes following are my questions? 1. 309L is for dissimilar metals but isn't 316L superior that 309L 2. Quantity of Mo in 309L is very low compared that to 316L. Is it ok to weld? It...

Thank you very much. You are great teachers for me.

OK got it but is there any restriction like if a welder is qualified for 6" pipe he cannot tack a 2" or lesser dia pipe? He cannot tack anything outer than his qualification limits for welding. Is it true or do we have any such reference?

Dear All, 1. In which asme section it is mentioned that tack welding should be done by a qualified welder? 2. Does any dia restriction applies for tack welding on the basis of his qualification range? Or a qualified welder on any range can to the tack welding or fitup of any range of dia and...