Thanks for all your responses. I plan on searching for a new frame to use in this application, it's not worth risking my life.
racookpe, see here:
Link
Thanks for the replies. Follow-up question:
If I had the frame powder-coated and cured at say, 400 degrees F, do you think that would help in stress-relief?
Greetings all.
I would like your opinion on an issue I am having. Would you consider a steel frame, such as a motorcycle chassis, that has been in a fire to be dangerous to re-use? My concern is that the fire has caused annealling in the steel and the curves and shapes of the steel frame may...