Can someone explain the technical justification for limiting the wall thickness for ASME IX procedures when toughness testing is required. I understand it being a supplementary variable. With that, why does API 1104 not require this restriction.
Thanks
Hello everyone, has anybody had experience GTAW on a side beam or seamer using an activating flux? I have been exposed to the FASTIG SS-7 use on stainless steels in the 7-10 gauge thickness range. Any thoughts on how this may affect the weld material properties? Visually it cleans up very...