Edstainless thank you for your response, i also think choosing a duplex stainless steel grade is the way to go. By the way the link you provided is a table for Aluminium Sulphate, my question was about Ammonium Sulphate.
Is 316 SS grade suitable for piping and equipment which will be exposed to ammonium sulfate slurry? At what flow velocity will erosion become a concern? I know there are several factors to consider including concentration of crystals, geometry of crystals, geometry of piping, temperature of the...
I would appreciate some input from the corrosion engineers here. If i have hydrogen gas flowing into a vessel, can it dissociate into atomic hydrogen and lead to hydrogen embrittlement, or does the hydrogen already have to be in atomic form (i.e. be the result of a corrosion reaction)? All input...