I have now dropped the idea buying second hand unit and am only looking into getting new workstation. I have read some good and some not so good stuff about HP workstations as PatCouture also mentioned. I am reading more about ZBooks reviews but since they come similar price with Dell...
Lot's of useful feedback here. I appreciate. Also i apologize for not providing enough relative information. For now i have found another solution for my problem though.
Thank You!
Hi.
I have come up with a solution that requires welding a metal arm to the extension screw of a bottle hydraulic jack. I was wondering what type of steel it is generally made of and if it is possible to weld it. It has to hold strong though.
Thanks in advance :)
Gtaw, Thank you for your response covering the subject in deeper manner. It took me quite a few times to read your post and translate it right, but really got some good answers - professional and clear as always.
Racookpe thanks for pointing out those things. The welding drawing with welded...
Hi again to everybody after a little brake. The last post was by me discussing some questions about welding geometry and general problems in welding QA process. It might look like this thread has been already faded, but I don’t see any reasons to think that way. I have received lots of good...
To GTAW
Thank you for excellent answers you provided again. An example of skewed t-joint was good way to make your point. I have very little experience with designing actual product drawings, so it was something worth to but in my bag of knowledge. I am though hesitating little bit if I am...
I am glad You found this thread helpful moltenmetal. Eng-Tip seems like a promising community from many aspects to all level of engineers. I picked out this community particularly to complement my studies and work related experience. Lots of welding specific forums out there but this one looks...
Thank you for your valuable feedback Al.
Your shared knowledge on different imperfections and how they can be influenced by cyclic stress, heat input and alignment of stresses is just those things I needed to know to get more clarification into understanding the strict standards in terms of...
Question 7
Sometimes when short fillet welds are welded a crater similar to end crater occurs anywhere within the length of the seam. When it doesn’t occur at the end of the weld I assume it should be assessed as a insufficient throat thickness rather than end crater. I wonder if it is...
dhengr:
Thank You for Your response and good words. It means lot to me get feedback from older and more experienced.
Yes, bringing in too many codes and requirements can make simple things look overly complicated. ISO standard is at the moment the best tool I have at my hands to get adequate...