When is required that all plates shall be supplied using the thermo-mechanical control process (TMCP), automatically the supply status of the material will be the type thermomechanically? If it instead the plates to be transformed into pipes, instead talking about Thermomechanically rolled? Is...

Thank you Jones. So is correct to consider that after tensile test the difference between weld material and the base material must be as minimum of 80MPa.

Dear All, The 80MPa of difference that this paragraph asks between base material and weld material, are to be considered after mechanical test or data Nominal tensile? Thank you in advance, Emilio A.

Hi, The material SA/A516 Gr.70 in accordance with ISO / TR 15608-2013 is classified as Subgroup 1.1 or 1.2? Thank you and regards, Emilio A.

Thank you... So for example the following composition in weld areas may be acceptable: Cr = 19.490 Ni = 43.570 Mo = 6.828 Nb = 2.411 Fe = 23.500 There is a reference in the Code governing these limits? Thanks, Emilio A.

Hello weldstan, Thanks for your cooperation. If I welding the B729 N08020 with the filler metal ENiCrMo-3, which chemical composition can I expect when I do the PMI (Positive Material Identification)? The Code Project is ASME B31.3. Grazie, Emilio A.

Hi, I can weld the B729 N08020 with the filler metal ENiCrMo-3? In the analysis of the chemical composition which composition must be taken into consideration, that of the filler metal or the base material? Thank you all. Emilio A.