Hi Ed,
As Al wouldn't be great as i'm trying not to use DLC (diamond like carbon) coatings as it is expensive when producing a fair amount.
Al wouldn't give use the strength we need without DLC.
I'm trying to maximize on strength, minimize weight and cost.
I'm currently looking at the M2...
Hi all,
I'm trying to find a steel alloy piston (gudgeon, wrist) pin that is a rating of 70 HRC (760 brinell hardness).
This steel must be able to be processed through nitriding chemical process to emphasizing the hard wearing properties of the carbon in the steel to the surface.
Steel stable...