Thanks a lot Mr.Pradip Goswami
I tried to upload my paper via attachment as mentioned above but not succeeded, any way here under the keywords of the paper as you mentioned it, you can downloaded from the web till i success ed to upload it.[S.S 316L STRESS CORROSION CRACKING OF VENTING SYSTEM...
Dear EdStainless
Thanks a lot for your fast response, i will send you my paper to clarify the problem, i think it will be more clear, then we will discuss the mater together, any way the idea to use SS316L and DUPLEX 2205 was from the construction company, we tried to solve the problem since...
sorry for lack of data, i will add the following:
our heat exchanger shell made of S.S 316L suffering from chloride induced stress corrosion cracking (CSCC) when exposed to a combination of tensile stresses, chlorides, water, oxygen, and a temperature. This heat exchanger tube type combined...