This I think will help out I am going to talk to my AI and welder to standardize a process for the shop. Thanks for your help.

The material is typically 1/4" or less for our industry so we can not stamp it as far as I remember from code there is a min were stamping is not allowed. The current Name plate they do not leave any moor on the pad it has so that would not be an option either unfortunately. I do see your point...

Working with my main welder he has a lot of experience but want to validate some information. We have a U1A and data plate that has a min shell thickness of .195 MFG of .395 corrosion allowance is 0 What does this mean for corrosion if I have pits/corrosion below MFG does it fail or is it...

Question regarding NBIC code. I have information from 2 sources 1 being my AI obviously I would follow my AI but wanted to ask the question. On a vessel repair name plate NBIC states the name plate must be adjacent to the original manufactures stamping/plate. Does this require welding to the...