Hello, All!
Thank you very much, this online collection of phase diagrams was exactly what I've been looking for.
Cu-Si might be a nice Idea, I'll definitively try that. Maybe even Cu-P, although I'm not entirely sure whether the copper borides I'm trying to make like the presence of phases...
Hello, Goahead,
Yes, I think the Ag/Cu eutectic might be a good idea. About non-eutectic alloys: I don't think that I will buy a brazing alloy but rather compose it from the elements.
On that welding-page you mentioned - is there information about the composition of those alloys? A quick...
Hello, All!
I'm trying to a solid-state chemical reaction in molten metal. Ideally I would use pure copper as this is included in my reaction anyway, but the oven I have available is not capable of sustaining the needed 1083°C. 1000°C is the limit it can handle.
I am therefore looking for a...