I am interested in finding a BPA free alternative for a juvenille beverage container. The product will be injection molded, come in varied translucent colors and need to have a decent impact resistance. Suggestions?
Thanks in advance
One more question:
When we originally received the parts they appeared hydrated and performed well. Am I correct that due to poor processing the parts de-hydrated much faster and to a greater degree than they should have? Is there any way to test the new parts that appear hydrated to see if...
Thanks for all the info. The reaction to Xenoy seems mixed so I'll try and describe my situation and see what you all think is the appropriate material.
- I am designing an electrical connector where two mating pieces flex to snap into the connection so higher flexural yield strength is...
Update:
Glass filled Nylon was selected for this part before I came on board. I am in the process of changing the material to Xenoy (1760E 11% glass filled) for it's flexural strength, resistance to chemicals and resistance to temperature fluctuations. I am trying to figure out what to do...
I am having problems with some parts that are Nylon 66 7% glass filled. After a period of time in a relatively low humidity environment, my parts are drying out and becoming very brittle. I am looking for two things:
a) Is there a way to predict how long it will take the parts to beome...