I want to get the B-H curve for 12L14 Carbon Steel. Is there anyone to know the information about the B-H curve?

I learn from this forum the annealing will improve the magnetic property of the carbon steel. So I want to do that. My question is that when is proper annealing time and that what temperature is set for annealing? In my case, I will machine the core part. To better magnetic performance, after...

My application is close to a Solenoid with air gap. The highest flux density in my circuit is about 2.0 Tesla. That takes place in guided material and I need about 0.6-0.7 Tesla in air gap.

My operation mode is in DC. However, depending on situation, DC signal should be changed frequently. I though AISI 1010. However, AISI 1010 is not avaible to me because I couldn't find any vendor to sell rod-type AISI 1010. So I need to think a subsitution for AISI 1010. I heard that silicon...

In my case, there is size and cost limitation. So I need to use higher permeability and not expensive materials so as to maximize the magnetic density.

What about using Silicon Steel instead of AISI 1010 or 1018?

How much temperature should be used for annealing AISI 1018?

I want to use AISI 1010 for electromagnetic purpose. However, I couldn't find any dealer and shop selling the AISI 1010 rod-type steel in USA. If anyone knows dealers, please let me know. Thanks in advance.