I end this forum here. I have gathered enough information regarding what i need. Thanks gentlemnen for helping me. Keep Posting. Krunal

Thank you Mates. This posts are valuable for me. However, Demon, I would like to ask you in particular: 1. What will be the cling, will it have any effect in the cling of the film? 2. What will be the effect on pinning? Will it cause loss of trims? 3. What should be the temperature...

I am using Metallocene in the core layer of a co-extruded (stretch film) cast film. The other two layers include a linear low density polyethene on one side and a low density polythene (anti cling layer) on the other. This give me a good film with good impact properties. The melt curtain is...

This was a real valuable information. Do you have some data to prove this? I tried to use the Nicolais and Narkis equation and my reading were well compatible to the equation. Are there any more theories support this? Thank you for your help. Regards, Krunal

Thank you Demon, I am working on Mechanical Properties of HIPS composites. I have one more query regarding this. If I add glass beads to the virgin matrix, effectively the yield strength should decrease. But in my case it increases. I do not know the reason. When I try to analyse, I find...

I am searching for the accurate value of virgin High Impact Polystyrene Material. Could any one help me please?