Hello everybody,
1)
I am sorry I have been away from this thread for so long and left you hanging with my "teaser".
Here is the answer to the question you have been waiting for...
Sample A is the "old" material. The one that shows much better resistance to corrosion.
Sample B is the "new"...
Hello everybody,
1)
Many of you suggested I get an analysis of both the old material and the new to highlight any potential differences.
2)
I followed this advice and I got the results.
SAMPLE A:
Carbon = 0.10%
Manganese = 0.51%
Silicon = <0.01%
Phosphorus = 0.008%
Sulphur = 0.011%
Chrominium...
Thanks again everybody,
1)
Like I said earlier, I am overwhelmed by the number and the quality of the replies I revceived for my post. For this reason, it will be impossible for me to answer specifically to all the questions I received. Nevertheless, I see a lot of commonalities between some...
Hello everybody,
1)
Wow, I am overwhelmed by how many and how good a response I am getting for my post.
2)
I am sorry I have not provided answers to your questions at this point. I have been working on other projects away from my computer.
3)
keep the good stuff coming, I should be able to...
Hello,
1)
As it is often the case, I am new to this "Eng-tips" forum because I have a question nobody will give me a straight answer to. Hope you guys will help.
2)
To make a long story short...
I am working for a conveyor manufacturer. To fabricate our conveyor rollers, we have been using...