Hi Yucao As you said, there is no detail in API about how to define corrosion loops. I will describe you what criteria I use to define my corrosion loops, which I had apply succesfully in different type off plants. First, I must say that I´m - What are corrosion loops?: corrosion loops are...

thank you Tom. I will chek articles in those places. Regards Luciano

Hello Steve What to recomend above is what i´m doing now. I´m using the API 581 2008 model to define the difrent variables we will need to collect to define a corrosion rate. Regards Luciano

Hello Ernie I understand what you are saying, and be sure that one of my recomendation is going to be to start using corrosion cupons. The objetive now is to have a first corrosion rate to stablish a base line. When I found that nace survey lynk, I thought that meaybe I could found similar...

This is what I found at NACE. I really didn´t see it so I´m not sure if it is what I´m looking for. http://events.nace.org/Publications/Corsur.asp#using Don´t worry, if I confirm this I wont give it to you so you can steel keep working. je regards Luciano

thanl you rustbuster I know that what i´m asking for is diffucult to find, that´s why i can´t find it!! I look up in NACE and I found that they have a corrosion rate survey for a lot of metals with different fluids. That could help, but it´s an expensive solution... Cheers

Hi I´m on a project where there is not too much information about the fluids proceced, and I need to propose a first estimation of corrosion rates. Do you know any book o bibliography where can I get standar corrosion rates for difrent systems on the oil production?? My first try was to use...