S235 is a structural steel and it will be difficult to reproduce this grade in a regular foundry. The Si content specified is 0.05% max, and it will be difficult controlling the melt.
What part are you attempting to convert using this grade. Perhaps, that may fetch more meaningful responses.
I'm just one step away from being rich, all I need now is money.
( read somewhere on the internet)
Arunmrao, thanks for your reply.
The only information i have to hand is that it is a 'runner wheel', I would suspect we are looking for reasonable abrasion resistance.
I will try to find more information presently.