Demagnetizing complex SS parts

[123Dog]

In some lab equipment 304 and 316 SS parts become magnetized just because of use
Now,, its out of the question to heat these parts for reasons of distortion
Is there any other way to demagnetize this lab equipment other than using heat
Thanks

 

[nbucska]

How big?

<nbucska@pcperipherals DOT com> subj: eng-tips
read FAQ240-1032

 

[EdStainless]

You can try it with AC demag, like you would after magneflux testing. With a complex shape it might not be possible to get real good deam though.

= = = = = = = = = = = = = = = = = = = =
Corrosion never sleeps, but it can be managed.

http://www.trenttube.com/Trent/tech_form.htm