Metal and wet chlorine gas

[musashi99]

Any ideas what materials (metal or coatings for metals)can hold up to wet chlorine gas for long periods of time? We have a custmer that needs a sensor that can hold up in that environment. The units he is currently using are not do the job.

Thanks

 

[EdStainless]

What is he using now?
What is his system built from?

The traditional solution would be a Ni-Cr-Mo alloy (C-22, 59, 686 or similar).

= = = = = = = = = = = = = = = = = = = =
Corrosion, every where, all the time.
Manage it or it will manage you.

http://www.trent-tube.com/contact/Tech_Assist.cfm

 

[JeroenPh]

Titanium also works in wet chlorine gas environment

 

[EdStainless]

But if it ever gets dry the Ti will burn.

= = = = = = = = = = = = = = = = = = = =
Corrosion, every where, all the time.
Manage it or it will manage you.

http://www.trent-tube.com/contact/Tech_Assist.cfm