nemat_hamedi
Mechanical
What is the best way to find microcracks on the surface due to electric discharge machining?
thanks
thanks
Eng-Tips is the largest engineering community on the Internet
Intelligent Work Forums for Engineering Professionals
-
Congratulations waross on being selected by the Tek-Tips community for having the most helpful posts in the forums last week. Way to Go!
MICROCRACK BY EDM 1
- Thread starter nemat_hamedi
- Start date
- Status
-
1
- #2
mfgenggear
Aerospace
It depends on the parent material.
Stainless steels would be flo or dye penetrant. It will verify surface indications.
On carbon base steels magnetic particle inspection.
EDM surfaces will have a recast surface and depending on the amperage of the burn
Will result more or less recast.
If I do use EDM, I will request less than .0005-.001 per surface then remove it.
If EDM house gets agressive in the burn
It will result in more recast layer.
Stainless steels would be flo or dye penetrant. It will verify surface indications.
On carbon base steels magnetic particle inspection.
EDM surfaces will have a recast surface and depending on the amperage of the burn
Will result more or less recast.
If I do use EDM, I will request less than .0005-.001 per surface then remove it.
If EDM house gets agressive in the burn
It will result in more recast layer.
mfgenggear
Aerospace
@nemat
did this answer your question?
did this answer your question?
- Status
Similar threads
- Locked
- Question
- Locked
- Question
- Locked
- Question
- Locked
- Question