Recent content by arivel

it's very simple . a cylinder inside a tube because the magnetic field must also be channeled in the return path

It's round but I don't want to use folded sheets. even solid rounds and 1002 steel tubes are not easy to find.

Hello and thanks for the reply . the motivation is always the same. I've also talked about it in other posts on this forum. This is an audio speaker field coil that runs on DC. Unfortunately, pure iron and cobalt steel are not only difficult to find but also very expensive. so I thought of...

Hi everyone . I would like to understand if it is possible to create an electromagnet in an iron-silicon alloy (FeSi). I don't have the equipment to do it myself so I thought of two different ways to proceed but I'm not an expert in these things and therefore I can't know if they are two viable...

but what you're saying ?

if I asked for a material with magnetic permeability it means that it is AC. it doesn't work in DC. what I wrote in the first message is clear, "without hysteresis". I didn't write: with little hysteresis.

what makes you think that the ferrite is free from hysteresis?

if you know they exist then why not post a link? ​

Hi everyone. can you advise me please? I am looking for a solid material without hysteresis with a relative magnetic permeability that goes beyond unity. I don't pretend that it is on par with permalloy or mu-metal but I can be satisfied with a value that is close to 10, if it surpasses it even...

its impedance changes with frequency

this is what I got using 15 connected toroids. I used a 20 - 20 Khz sweep signal and as you can see the user is a speaker. no amplification of the signal coming from the current sensor. Don't ask me how much current I passed because I didn't...

50mA peak-to-ground voltage. each toroid is wrapped in many turns of wire but only one layer. this is because for the moment it is a test that I want to do to see what we get. if the result is satisfactory I can even do more than one lap. remember that I have to wind many toroidal rings all by hand.

@3DDave AC

no

sorry but there are some errors. each individual toroidal ring measures an inductance of 0.0000013H the copper enamelled wire has a section of 0.2 mm