  1. bob330

    Thermal conductivity of duplex

    EdStainless, The stuff on the Al website simply looks like typo stuff where they apparently took austenitic SS CTE data and gave out those same numbers for other materials like 2205 and 440A stainless which we all know do not expand nearly as much. I didn't check too many other materials but...
  2. bob330

    Section VIII Div 1 versus Div II

    Thanks to all you guys.
  3. bob330

    High Carbon in 310SS

    Hi All, I noticed that the specification for 310SS allows up to .25 wt% carbon which is three times that of a standard grade like 304. Would it be fair to say that this alloy is extremely amenable to being sensitized during welding? Is there any information on this in the technical...
  4. bob330

    Appendix HA

    Hi Guys, Near the beginning of the Section VIII code section UHA, it referes to appendix HA for tips on the usage of stainless steel. However, I could not find appendix HA. Does anybody know which document to locate this from? Bob
  5. bob330

    Thermal conductivity of duplex

    Thanks sreid, I wonder how many metallurgical folks have been fed severe misinformation on that A-L website. When they said that that 440A had the same thermal expansion properties as austenitic SS, I knew something was wrong. Add that to them showing the 2205 to have the same CTE as...
  6. bob330

    Section VIII Div 1 versus Div II

    Hi Guys, What is the difference between Section VIII div 1 and Div 2? Also, what is the differnce between allowable stress value "S" and design stress intensity "Sm"? Thanks, bob
  7. bob330

    Thermal conductivity of duplex

    Also Guys, The CTE data for 440A stainless steel is also completely wrong. I would recommend you all avoid the AL website for technical information. Bob
  8. bob330

    Thermal conductivity of duplex

    Thanks Guys, The Alleheny Ludlum site referenced above is all screwed up as they report CTE values for 2205 as being identical to those of 316SS /317 SS. Why does this stuff happen? Their site is very misleading. There is no excuse for this nonsense. Bob
  9. bob330

    Allowable Stresses at High Temperature

    Thanks, This does not make a lot of sense, I have several separate references that show 10,000 and 100,000 hour rupture data for 316, 316L and 321 SS and the 316L is equal to or superior in rupture strength to 321SS at all the higher temps 900F-1500F and only slightly iunfereior to regular...
  10. bob330

    Allowable Stresses at High Temperature

    Guys, Where in the ASME code would I find allowable stres values for common austenitic SS materials at higher temperatures like 900F-1500F. Does the code mandate lower allowable stress values for the "L" grades versus the regular grades and how does 316L compare to say 321SS or 347SS? Bob
  11. bob330

    Pitting of 316L in seawater

    Thanks Guys, Stagnancy and fouling are no doubt the big concerns. I did want to clarify someting here that I was not celar about earlier. The tube side service is cooling tower water and the 1000ppm chloride is a maximum potential condition and in the past has only reached these levels...
  12. bob330

    Residual Stress peaks versus welding technique

    Thanks to all of you guys, We are going to do our first internal inspection at a one year time frame instead of the origianlly planned 1.5 to 2 year plan. This will give us at least somewhat improved piece of mind. Although we have not really observed caustic SCC in this vessel, the...
  13. bob330

    Are 317LM and 317LMN ASME approved Materials

    Thanks Guys, I had a typo there......sorry. Actually I am writing a German to American alloy translation page and UNS S31725 is essentially equivalent to German alloy 1.4449. I wanted to add a comment in my guide as to whether or not the ASME recognized all the US equivalents of the German...
  14. bob330

    Are 317LM and 317LMN ASME approved Materials

    Hi Guys, I was wondering if 317LM (UNS S31735) and 317LMN (UNS 31726) are ASME pressure vessel code approved or recognized materials available with "SA" designations? Bob
  15. bob330

    Thermal conductivity of duplex

    Hi All, For heat exchangers, how does the thermal conductivity of duplex grades like 2205 compare to that of austenitic grades and plain carbon steels? Bob
  16. bob330

    Weld penetration CS versus SS

    Hi All, Given a certain diameter rod and amperage, is there more penetration into austenitic SS or plain carbon steel materials when welding. I guess another way of asking this is to ask whether or not root face heights (at weld prep) should be made bigger or smaller for SS as compared to...
  17. bob330

    Pitting of 316L in seawater

    Thanks for the input guys, I did find a chart that disagrees with your recommendations here and shows that there is little propensity towards 316 pitting at any concentration of Chlorides at temperatures below 50C. However, this chart probably does not consider any crevice behaviour. This...
  18. bob330

    Pitting of 316L in seawater

    Hi, Will 316L tend to pit in stagnant seawater at ambient temperatures if there is no fouling deposits or crevices present on it? If not, would we expect to see issues with fouling present? Also, would anybody expect to see pitting for tube side water in an HE application with up to...
  19. bob330

    Residual Stress peaks versus welding technique

    Thanks all, I did want to mention that there is information in the technical literature saying that carbon steel actually becomes more susceptible to caustic SCC as it gets softer believe it or not!!! Thus fully decarburized surfaces are more susceptible than normal pearlitic/ferritic...
  20. bob330

    Rust formation on 316 bolt

    EdStainless, When you say improperly cleaned or handles, what exactly do you mean? Is it impossible to get the red corrosion products if the steel had been passivated correctly or can certain environments bring it out regardless? Also, does stainless steel really need to be passivated prior...