Great answer dbooker630, this helps me move my company in the correct direction and get “for reference only” removed from gauges that actually determine a parts conformance to print. I am still annoyed why the ISO 9001 surveillance auditor allowed such a blatant misinterpretation to exist for...

Thanks for the informative posts. Perhaps I was vague in my question. Where does it state what instrument/gauge is to be calibrated. What is the criterion for calibration? A nice simple answer would be helpful. Thanks Again!

Pertaining to control of measurement devices. I just started work for a new company which is ISO 9001 certified and they are trying to get away without calibrating measuring instruments by labeling everything but a few micrometers and calipers "For Reference Only". I can’t find a clear...

Greetings, For a Semi-tubular rivet, is there a specification as to the condition of the formed end of the rivet. Such as, if I was inspecting parts connected with a Semi-tubular rivet what guidelines dictate a pass / fail for the formed end. I have found much information on the rivets(ASME...

Thanks for the replies. I posed this question for discussion only, probing to see if any quality professionals have the same concerns as me. I am not a newbie, I have set-up ISO 9001, AS9100, NADCAP, TS16949 QMS systems for companies over the last 15 years working as an employee and sometimes...

I would like to present a topic for discussion. The elimination of registration to ISO 9001-2008 Quality Management Systems. If a company followed the ISO 9001-2008 as a guideline for their QMS and used this system to its fullest with the discipline required to gain the most out of it but...

????? or Thank you very much for the advice. I am a quick study!!

Clarification on increasing my marketability. I am a quality engineer/manager well versed in statistics, lean manufacturing, and six sigma tempered with 20 years experience in the metals fabrication industry with a proven list of accomplishment applying these skill sets. With the current...

Thank you all very much. Mandarin came up a lot in my research as to what dialect is used in the industrialized regions. I am off to Mandarin Chinese lessons. Hmm? Chinese with a Boston accent.

What would be the most useful Chinese dialect for a Quality Engineer to learn? The reason is to make myself more marketable. I have 13 years in Quality Engineering and a total of 26 years of Engineering in metal fabrication and welding.

Thanks to all for settling this debate. Much appreciated, Dave

Situation, if one has a 1 inch diameter x 6 inch long solid brass bar and a ¼ diameter hole was drilled in the center of the solid brass bar, now if the brass bar was heated to 1000 F would the ¼ hole expand or contract? Thanks, Dave

The business I owned and operated was set up to only to weld reactive metals such as Titanium, Zirconium, and Molybdenum. I used a Vacuum Atmospheres hermetic welding chamber which maintained and atmosphere of Argon with less than 20-ppm O2 and 20-ppm moisture. This unit is stainless steel...

Thanks for the input. I am familiar with ISO TS 16949 and ISO.org. I see you copy and pasted your reply from the abstract on ISO.org. Thanks anyway.

The request for TS 16949 is from a new customer with high volume potential. The automotive customer is a new prospect not our standard customer base. If we want their automotive work we must be TS 16949. As far as existing customers I do not believe any specifically requested ISO 9001-2000...

Would it make sense for a company that is ISO 9001-2000 certified, and has been told by a big customer, that it must get TS 16949 to abandon the ISO 9001-2000 cert and get the TS 16949 cert and use this as its sole QMS. Thus alleviating the expense of operating two QMS systems. I know TS 16949...

Our company is in the process of acquiring a European Pressure Directive (PED). We manufacture pressure monitoring and switching devises. The T.U.V. representative /auditor stated that the only faculty authorized to perform weld testing is in Ohio. Is this correct? Any thoughts on the subject...

Thank you PVINSPECTOR , I have read article III and have drawn the conclusions you have mentioned. Not working with ASME IX on a daily basis and without the benefit of any training as to the interpretations led me to seek conformation. Thanks again you have been very helpful. Best Regards,

Could someone please explain the process of certifying a welder to ASME IX. We are only using ASME as a guide for our welding system. Does one start with a WPS that specifies the welding conditions then one fills out the PQR with the actual welding data used on a weld coupon then the WPS and...

The alloy TP316, what does the TP stand for? Thanks, Dave