Folks, I am doing small piece of work on Riser Replacement assessing the feasibility of wet storing the risers for a minimum of 3 months before the FPSO arrives on site. The carcass material is 316L which is generally unsuitable for wet storage. It has been proposed that this can be mitigated...

Folks, Any ideas of what auses the pitting corrosion on wet gas carbonsteel pileline? Any feedback would be appreciated. Please see attached

ndeguy; Thank you!

enmax, Thank you and all the best of 2011

rustbuster; thanks for replying back,the corrsion mechanism is Preferential Weld Root Corrosion and yes we do use a corrsion inhibitor. however there are no historical date with regards to the corrosion inhibitor performance over the root of pipeline welds! SJones: thanks

Hi Guys, The management raised concerns that the nickel content of welding consumables used in the construction of one of our gas Production Pipeline (1.5% Ni) may give rise to unacceptably high corrosion risks by promoting Preferential Weld Root Corrosion (PWC). My question is : what will be...

Thank you EdStainless

Dear All, I work with a client and they found out that cement was spilled onto the process piping on the platform! Can any one verify if this can do any harm to the piping because it is very difficult to remove this. Thanks in advance

Thank you to everyone who responded, Your input was much appreciated

Dear All, The company I work for operates a dry gas pipeline, I was just wondering can we inject the pipeline with corrosion inhibitor to control corrosion (If any) and how can we monitor the corrosion, please note that pigging is not an option. Your help is much appreciated

Add to SJohns, the only method to monitor the corrosion in subsea pipeline is pigging.

and the only way to monitor the corrosion in subsea line is pigging

Hi, Please check out the link below: http://www.matthews-training.co.uk/ Hope this helps

Hi AO1958, Nitrogen compound(Ammonia..etc) can cause a localized corrosion to the copper/copper alloy

Hi AO1958, Any compound with nitrogen (Like Ammonia,...etc) can casue a localizes corrosion to copper/copper alloy

Xeros, Try iicorr ltd, please find the link below: http://www.iicorr.com/

Hi, Try: European Corrosion Supplies Ltd or: iicorr ltd