Unclesyd- You are very precise about the heat treat routing. YOu had run into this requirement before? Thanks a lot.

Edstainless. You got it. That is exactly what I wonder too. See the link below or the attached article. http://toolingandproduction.com/archives/0500/0500tn.asp Heat treatment of tool steels By Ed Tarney, Crucible Service Centers Syracuse, NY Most punches, dies, stamps, and other...

NickE. Thank you. Your guys are all wonderful and helpful. The only info that we got are the material (L6), hardness requriment (HRc 28-32) and dimensions. Who normally details the heat treat routing, the customers and supplierS? We don't know if any info is missing from the original request. We...

Thank you EdStainless. We are going thru middle man and that is what makes tough to communicate directly with customer. A purchasing agent is what we are dealing with now and have no knowledge of heat treat and the material. We don't see a justification for any heat treat between rough and...

unclesyd , Thank you so much for getting back to me. Yes, I do owe you details and very desperate for information as we are approaching the deadline. We are providing the rough machined forge part to the customer. According to A681-94, the max hardness that we can get by annealing only is...

Can you achieve RC28-34 for L6? And how? Rough and finish machining are to be followed. Thanks.

Does anybody have any experience of using SS304 matl for a banjo bolt?