  1. Maffei

    BIMETALLIC CORROSION PROBLEM

    Military Standard (MIL-STD-889) would be a good start. Vince Maffei
  2. Maffei

    Help on Aluminum

    The following is the compositional differences between 1100 and 1200: 1100 .95Si+Fe, .05-.2Cu, .05Mn, .10Zn, .05others 1200 1.0Si+Fe, .05Cu, .05Mn, .10Zn, .05Ti, .05others Vince
  3. Maffei

    What happens to the strength of aluminum, A356 T6, after welding

    If welding in the T6 condition, you will loose properties in and around the weld area. The properties in the welded area will be comparable to those in the annealed condition. In addition, when welding in T6 (if welding is significant)you may induce stress which may result in cracks. In...
  4. Maffei

    Welding of dissimilar metals

    I need some information on welding 430 (or 430F) stainless steel to 304 or 316. Is it possible using TIG, beam or laser welding? What are the concerns when welding these materials together if any? What filler rod is recommneded? Any other information would be greatly appreciated Thank You...
  5. Maffei

    Welding of dissimilar metals

    I need some information on welding 430 (or 430F) stainless steel to 304 or 316. Is it possible using TIG, beam or laser welding? What are the concerns when welding these materials together if any? What filler rod is recommneded? Any other information would be greatly appreciated Thank You...
  6. Maffei

    Welding of dissimilar metals

    I need some information on welding 430 (or 430F) stainless steel to 304 or 316. Is it possible using TIG, beam or laser welding? What are the concerns when welding these materials together if any? What filler rod is recommneded? Any other information would be greatly appreciated Thank You...
  7. Maffei

    Metallurgy of stainless steel welding

    I need some information on welding 430 (or 430F) stainless steel to 304 or 316. Is it possible using TIG, beam or laser welding? What are the concerns when welding these materials together if any? What filler rod is recommneded? These are just some of the questions. Thanks Vince Maffei