BIMETALLIC CORROSION PROBLEM

[Zygfeld]

To anyone who knows about this stuff...

Is there anywhere a list showing corrosive properties between metals. I need to know if the metals I am working with will be corrosive if I place them together. I work with a variety of carbon steels, stainless steels, coppers, etc. It would be invaluable to me to simply have a list in front of me to reference to see if the combonation I am proposing is feesible.

Thank you very much,

Zygfeld

 

[Maffei]

Military Standard (MIL-STD-889) would be a good
start.

Vince Maffei

 

[Rich2001]

Here is a link to one such chart. Galvanic corrosion

http://www.pemnet.com/design_information/galvanic.html

The chart from Mil Std 889

http://www.eaa1000.av.org/technicl/corrosion/galvanic.htm

Another location to get more info

http://www.nace.org/

Have a good day,
Rich

 

Maybe you can try the website:

http://www.corrosionsource.com/handbook/galv_series.htm